Fatigue-life and stress distribution of a glass-ceramic under different loading conditions

Abstract This study aimed to evaluate the effect of different loading conditions on the mechanical behavior and stress distribution of a leucite-reinforced glass-ceramic. Plate-shaped ceramic specimens were obtained from leucite-reinforced glass-ceramic (1.5 × 8.4 × 8.3 mm) and adhesively cemented to a dentin analog substrate. Monotonic and cyclic contact fatigue tests were performed to simulate sphere-to-flat contact, using a 6 mm diameter spherical piston; and flat-to-flat contact, using a 3 mm diameter flat piston. For the monotonic test (n=20), a gradual compressive load (0.5 mm/min) was applied to the specimen using a universal testing machine. Failure load data were analyzed with Weibull statistics. The cyclic contact fatigue test was performed using protocols (load and a number of cycles) defined by the boundary technique (n=30). Fatigue data were analyzed using an inverse power law relationship and Weibull-lifetime distribution. The stress distribution was investigated using Finite Element Analysis (FEA). The monotonic and the fatigue Weibull modulus were similar among the two contact conditions. In fatigue, the slow crack growth exponent was greater for sphere-to-flat contact, which indicates that the load level had a greater effect on the specimen's probability of failure. In conclusion, FEA showed different stress distribution for the tested loading conditions. The stress distribution and probability of fatigue failure of specimens tested in sphere-to-flat contact showed greater dependency to load level.

Resumo O objetivo deste estudo é avaliar o efeito de diferentes condições de carregamento no comportamento mecânico e na distribuição de tensões de uma vitrocerâmica reforçada com leucita. Amostras cerâmicas em forma de lâminas foram obtidas a partir de vitrocerâmica reforçada com leucita (1,5 × 8,4 × 8,3 mm) e cimentadas adesivamente a um substrato análogo de dentina. Ensaios de carga de compressão monotônica e fadiga foram realizados para simular o contato esfera-plano, usando um pistão esférico de 6 mm de diâmetro; e contato plano com plano, usando um pistão plano de 3 mm de diâmetro. Para o ensaio de carga de compressão monotônica (n=20), foi aplicada uma carga compressiva gradual (0,5 mm/min) ao corpo-de-prova usando uma máquina de ensaio universal. Os dados de carga de fratura foram analisados de acordo com a distribuição de Weibull. O teste de fadiga foi realizado com os protocolos (carga e número de ciclos) definidos pela técnica de boundary (n=30). Os dados de fadiga foram analisados usando uma relação de tempo de vida - tensão de lei da potência inversa (IPL- inverse power law). A distribuição de tensões foi investigada usando análise de elementos finitos (AEF). O módulo de Weibull para teste de compressão monotônico e de fadiga foram semelhantes entre as duas condições de contato. Em fadiga, o expoente de crescimento sub-crítico da trinca foi maior para o contato esfera-plano, o que indica que o nível de carga teve um efeito maior na probabilidade de falha do corpo-de-prova. Em conclusão, AEF apresentou distribuição de tensões diferente para as condições de carregamento testadas. A distribuição de tensões e a probabilidade de falha em fadiga dos corpos-de-prova testados utilizando o contato esfera-plano apresentaram maior dependência do nível de carga.

Failure behavior of zirconia crowns subjected to air abrasion with different particle sizes

Abstract This study aimed to investigate the failure behavior of 3 mol.% yttria-stabilized tetragonal zirconia polycrystal (3Y-TZP) prosthetic crowns air-abraded with aluminum oxide (AO) particles of different sizes. Ninety ceramic premolar crowns were produced with 3Y-TZP frameworks veneered with porcelain. Crowns were randomly divided into three groups, according to the size of the air abrasion AO particles (n = 30): (GC) untreated (control); (G53) 53 µm; (G125) 125 µm. Air abrasion was performed with 0.25 mpa pressure, 10-mm distance, for 10 s. Crowns were adhesively cemented to dentin analog abutments. Specimens were loaded in compression to failure, in 37oC distilled water, using a universal testing machine (n = 30). Fractographic analysis was performed using a stereomicroscope and SEM. The roughness of the crown's inner surface was evaluated using an optical profilometer (n = 10). Fracture load data were statistically analyzed with Weibull analysis and roughness data with Kruskal-Wallis (α = 0.05). GC had the lowest characteristic fracture load (L0), while G53 and G125 had higher and statistically similar L0 values. The Weibull modulus (m) was similar among groups. The failure modes observed were catastrophic failure and porcelain chipping. There were no differences between the roughness parameters for the experimental groups (p > 0.05). The size of the AO particles did not affect the fracture load and failure mode of 3Y-TZP crowns. Air abrasion with 53 µm and 125 µm particles resulted in a higher fracture load of ceramic crowns than the untreated group while maintaining their reliability and surface characteristics.

Resumo O objetivo deste estudo foi investigar o efeito do jateamento com óxido de alumínio (AO) com diferentes tamanhos de partículas no comportamento de fratura de coroas protéticas de zircônia tetragonal estabilizada com 3 mol% de ítria (3Y-TZP). Noventa coroas cerâmicas de pré-molares foram produzidas com infraestruturas de 3Y-TZP recobertas com porcelana. As coroas foram divididas aleatoriamente em três grupos, de acordo com o tamanho das partículas de AO do jateamento (n = 30): (GC) não tratada (controle); (G53) 53 µm; (G125) 125 µm. O jateamento foi realizado com pressão de 0,25 MPa, distância de 10 mm, por 10 s. As coroas foram cimentadas adesivamente em pilares análogos à dentina. As coroas foram testadas em compressão até a falha, em água destilada a 37ºC, usando uma máquina universal de ensaios (n = 30). A análise fractográfica foi realizada usando estereomicroscópio e MEV. A rugosidade da superfície interna das coroas foi avaliada usando um perfilômetro óptico (n = 10). Os dados de carga de fratura foram analisados ​​estatisticamente com análise de Weibull e os dados de rugosidade com Kruskal-Wallis (( = 0,05). GC apresentou a menor carga característica de fratura (L0), enquanto G53 e G125 apresentaram valores de L0 maiores e estatisticamente semelhantes. O módulo de Weibull (m) foi semelhante entre os grupos. Os modos de falha observados foram falha catastrófica e lascamento da porcelana. Não houve diferenças entre os parâmetros de rugosidade para os grupos experimentais (p > 0,05). O tamanho das partículas de AO não afetou a carga de fratura e o modo de falha das coroas 3Y-TZP. O jateamento com partículas de 53 µm e 125 µm resultou em maior carga de fratura das coroas cerâmicas do que o grupo não tratado, mantendo sua confiabilidade e características de superfície.

Morse taper performance: A finite element analysis study

OBJECTIVES: To evaluate and compare the magnitude and distribution of stresses generated on implants, abutments and first molar metal-ceramic crowns using finite element analysis. METHODS: Preliminary three-dimensional models were created using the computer-aided design software SolidWorks. Stress and strain values were observed for two distinct virtual models: model 1 - Morse taper and solid abutment; model 2 - Morse taper and abutment with screw. A load (250 N) was applied to a single point of the occlusal surface at 15° to the implant long axis. Von Mises stresses were recorded for both groups at four main points: 1) abutment-retaining screws; 2) abutment neck; 3) cervical bone area; 4) implant neck. RESULTS AND CONCLUSION: Model 1 showed a higher stress value (1477.5 MPa) at the abutment-retaining screw area than the stresses found in model 2 (1091.1 MPa for the same area). The cervical bone strain values did not exceed 105 µm for either model.

Características mecânicas e ópticas de resinas bulk-fill: revisão de literatura / Mechanical and optics characteristics of bulk-fill resins: literature review

Objetivo: realizar uma análise descritiva das característicasmecânicas e ópticas das resinas bulk-fill com baseem dados da literatura. Revisão da literatura: para arealização do estudo, foram utilizados artigos extraídosdas bases de dados PubMed, SciELO e Lilacs. As palavras-chave utilizadas para busca foram: resina bulk-fill,resina composta, polimerização, grau de conversão,caracterização, dureza, rugosidade, resistência à flexão,translucidez, propriedades ópticas. Os compostosbulk-fill são basicamente formados por matriz orgânicae partículas de alumínio, silício e bário, medindo de0,1 µm a 1 µm. Tratam-se de resinas translúcidas quepodem ser polimerizadas adequadamente em camadasespessas, possuem propriedades mecânicas aceitáveis,porém inferiores às resinas nano e micro-híbridas, e têmbaixo grau de contração volumétrica e menor tensão decontração do que as resinas compostas convencionais.Considerações finais: as resinas bulk-fill são indicadaspara restauração de cavidades com fator de contraçãocavitário desfavorável. A cobertura dessas resinas com2 mm de resina composta convencional em área oclusalé recomendável. (AU)

Objective: the objective of this work was, based on literature data, to describe mechanical and optical characteristics of bulk-fill resins. Literature review: articles were selected at PubMed, SciELO and Lilacs. Search was performed using the keywords: bulk-fill resin, composite resin, polymerization, degree of conversion, characterization, hardness, roughness, flexural strength, translucency, optical properties. Bulk-fill composites are basically formed by organic matrix and particles of aluminium, silicon and barium, measuring from 0.1 µm to 1 µm. They are translucent resins that can be polymerized in thick layers, with acceptable mechanical properties, but with inferior performance than nano and microhybrid resins. The material presents volumetric lower shrinkage and residual stresses than conventional composite resins. Final considerations: bulk-fill resins are indicated for the restoration of cavities with an unfavorable contraction factor. A 2 mm-thick layer of conventional composite resin at the occlusal area over the bulk-fill resins is recommended. (AU)

Self-assessed oral health of elderly using complete dentures

Com o aumento da longevidade da população e a potencial relação entre a idade e perda de dentes, existe uma necessidade crescente da substituição de dentes por proteses totais. O impacto das próteses totais na saúde bucal de idosos é de grande importância para sua saúde geral. Objetivo: o objetivo deste estudo foi analisar a autopercepção sobre saúde bucal de usuários de próteses totais. Métodos: o instrumento utilizado foi o questionário GOHAI (Índice de Avaliação Geriátrica de Saúde Oral), contendo 11 questões específicas sobre aspectos físicos e psicológicos (conforto ao comer, dor, dificuldades em morder, mastigar ou engolir alimentos, dificuldade de fonação, limitação nos contatos sociais, cuidados com autoestima e aparência). As proteses totais foram avaliadas de acordo com o índice Nevalainen, incluindo aspectos de retenção, estabilidade, dimensão vertical e oclusão. Sessenta voluntários frequentadores de um Departamento de Atenção aos Idosos concordaram em participar do estudo. Resultados: a pontuação média do GOHAI foi 25, ou seja, notou-se uma baixa autopercepção de saúde bucal. A saúde bucal foi classificada como insatisfatória, apesar da qualidade ou tempo de uso das próteses totais ou da idade que a pessoa tinha quando começou a utilizar as próteses totais. Conclusão: conclui-se que os escores GOHAI não foram afetados pela estabilidade ou retenção das próteses totais. Com o aumento na longevidade e a potencial relação entre a idade e a perda de dentes, há uma necessidade crescente de substituição dos dentes por próteses totais. O impacto das próteses totais na saúde bucal de idosos é de grande importância para sua saúde geral...

With the increase on population longevity and the potential relationship between age and teeth loss, there is a rising need for teeth replacement with complete dentures. The impact of dentures using on older adults oral health is of great importance for general health. Aim: the objective of this study was to evaluate self-assessed oral health of older adults using complete dentures. Methods: the instrument used for this evaluation was GOHAI (Geriatric Oral Health Assessment Index) questionnaire, containing 11 specific questions of physical and psychological aspects (such as eating comfort, pain, troubles in biting, chewing or swallowing foods, talking issues, limitation is social contacts, oral health care, self-esteem, appearance). Complete dentures were evaluated according to Nevalainen index, including retention, stability, vertical dimension, articulation and occlusion aspects. Sixty participants (n=60) agreed in participating on the study, from Department of Attentionto Older Adults. Results: mean GOHAI score was 25, meaning a low self-perceived oral health. Oral heath was reported as unsatisfactory, despite the quality or time in use of complete dentures or the age the person had when start using dentures. Conclusion: we conclude that GOHAI scores were not affected by dentures stability and retention...

Degree of chronic orofacial pain associated to the practice of musical instruments in orchestra's participants.

Objective: The practice of playing musical instruments can affect structures of the head, neck, mouth, and the masticatory system. The aim of this study was to obtain information regarding the prevalence of orofacial pain in musicians according to the type of instrument they play, by applying a specific questionnaire. Materials and Methods: One hundred and seventeen musicians of Sao Paulo state's orchestras participated in this study. They answered an anamnesis questionnaire with 20 questions regarding their personal data, type of instrument played, hours of daily practice, and presence or absence of orofacial pain according to the Chronic Pain Grade Classification (CPGC). Musicians were divided into two groups in accordance with the risk of affecting TMJ: RG (risk group, including violin, viola, vocalist, trombone, tuba, clarinet and saxophone); CG (control group, other instruments). They received an informative brochure about the subject. Data obtained from the questionnaire were submitted to descriptive statistics, Pearson's correlation analysis and Z-test for difference between two proportions. Results: The participants were from 15 to 62 years old. Pain degree showed positive correlation for reported symptoms (P = 0.002) and hour/day practice (P = 0.030). Regarding the prevalence of pain degree, data were, for RG: Grade 0 (54.5%), Grade 1 (30.3%), and Grade ≥2 (15.1%). For CG, Grade 0 (84.4%), Grade 1 (8.9%), and Grade ≥2 (6.6%). Z-test showed positive difference between groups (P = 0.0001). Conclusion: It was concluded that the musicians of risk group presented higher prevalence of orofacial pain than control (non-risk) group.

Métodos de caracterização de materiais para pesquisa em odontologia / Materials characterization methods in dentistry research

Esta revisão tem por finalidade esclarecer alguns pontos relevantes a respeito de algumas técnicas utilizadas em odontologia para caracterização dos materiais. Após um levantamento bibliográfico de 2006/2011 na base de dados PubMed, a microscopia eletrônica de varredura e a espectroscopia no infravermelho por transfor mada de Fourier foram as técnicas mais utilizadas para cada método de caracterização (microscopia e espectroscopia). Porém, outras técnicas têm sido utilizadas na caracterização dos materiais na pesquisa em odontologia.

Fratura precoce da porcelana em restaurações com infra-estrutura de zircônia: influência de gradientes térmicos no desenvolvimento e magnitude de tensões residuais e transitórias / Porcelain fracture in veneered-zirconia restorations: influence of thermal gradients on the development and magnitude of residual and transient stresses

Esse estudo avaliou o desenvolvimento de tensões dentro da porcelana de restaurações metalo-cerâmicas (MC) e de zircônia-porcelana (ZC) como resultado de diferentes taxas de resfriamento a partir de temperaturas acima da transição vítrea (Tg). Restaurações unitárias (coroas) foram fabricadas com 1 ou 2 mm de espessura de porcelana. Termopares foram posicionados nas superfícies de cimentação (T1) e oclusal (T4) e inseridos na interface (T2) e dentro da porcelana (T3). Para o resfriamento rápido, o forno foi aberto imediatamente após o tempo de sinterização e desligado. O resfriamento lento foi obtido pela abertura do forno quando a 50°C abaixo da Tg. Modelos axi-simétricos foram construídos para simulação de tensões térmicas tempo-dependentes usando análise de elementos finitos (AEF). Equações de temperatura em função do tempo obtidas por termopares foram inseridas no modelo como condições das margens. A mudança do coeficiente de expansão térmica, densidade, módulo de cisalhamento, capacidade térmica e da Tg de acordo com a taxa de resfriamento foi considerada para simulação do comportamento da porcelana em temperaturas acima da Tg (visco-elástico). O comportamento dos materiais de infra-estrutura e da porcelana abaixo da Tg foi considerado elástico. A taxa de resfriamento na faixa de temperatura próxima a Tg foi 20°C/min e 900°C/min para resfriamento lento e rápido. Durante o resfriamento lento, os diferentes termopares mostraram temperaturas similares em ambas as coroas. Gradientes de temperatura foram observados no resfriamento rápido da coroa ZC (T1-T4 = 100°C) e, em menor magnitude, para a MC (T1-T4 = 30°C). Os resultados de AEF mostraram diferenças de tensão residual na porcelana sobre zircônia e sobre metal para resfriamento rápido (25 MPa) e lento (15 MPa). Tensões transitórias com magnitude de até 200 MPa foram observadas dentro da porcelana quando resfriada rapidamente, enquanto foram de magnitude insignificante no resfriamento lento. As tensões ...

This study evaluated the development of transient and residual stresses within the porcelain of veneered restorations (zirconia- and metal-based) as a result of different cooling rates from temperatures above the glass transition temperature (Tg). All-ceramic (porcelain on zirconia-based ceramic) and porcelain-fused-to-metal (PFM) molar crowns were fabricated with 1 mm or 2 mm porcelain thickness. Thermocouples were attached to intaglio (T1) and occlusal (T4) surfaces and embedded within the ceramics interface (T2) and inside the porcelain (T3) to acquire temperature readings by time. For fast cooling, the furnace was opened immediately after the holding time and switched off afterward. Slow cooling was determined by opening the furnace when it reached 50 °C bellow the Tg. Axially-symmetric crown-like models were constructed to perform a simulation of time-dependent thermal stresses using finite element analyses (FEA). Time-dependent temperature equations from thermocouples were set as boundary conditions for surfaces of the model. Coefficient of thermal expansion, density, shear modulus, heat capacity and Tg dependency on cooling rate were considered for the porcelain simulation (visco-elastic above Tg). Porcelain below the Tg and the framework materials were considered to behave elastically. The cooling rates at Tg range were 20 °C/min and 900 °C/min for slow and fast cooling. During slow cooling, different thermocouples showed similar temperatures for both zirconia and metal crowns. Remarkable temperature gradients were observed for the fast cooled all-ceramic crown (T1-T4 = 100 °C) and, of lower magnitude, for PFM (T1-T4 = 30 °C). FEA results showed differences between residual stress observed for porcelain on zirconia and on metal for fast (25 MPa) and slow cooled crowns (15 MPa). Significant transient stress waves (up to 200 MPa) were observed within the porcelain during fast cooling through the Tg, while they were insignificant for...

Flexural and diametral tensile strength of composite resins

This study evaluated the flexural strength (sf) and the diametral tensile strength (st) of light-cured composite resins, testing the hypothesis that there is a positive relation between these properties. Twenty specimens were fabricated for each material (Filtek Z250- 3M-Espe; AM- Amelogen, Ultradent; VE- Vit-l-escence, Ultradent; EX- Esthet-X, Dentsply/Caulk), following ISO 4049 and ANSI/ADA 27 specifications and the manufacturers’ instructions. For the st test, cylindrical shaped (4 mm x 6 mm) specimens (n = 10) were placed with their long axes perpendicular to the applied compressive load at a crosshead speed of 1.0 mm/min. The sf was measured using the 3-point bending test, in which bar shaped specimens (n = 10) were tested at a crosshead speed of 0.5 mm/min. Both tests were performed in a universal testing machine (EMIC 2000) recording the fracture load (N). Strength values (MPa) were calculated and statistically analyzed by ANOVA and Tukey (a = 0.05). The mean and standard deviation values (MPa) were Z250-45.06 ± 5.7; AM-35.61 ± 5.4; VE-34.45 ± 7.8; and EX-42.87 ± 6.6 for st; and Z250-126.52 ± 3.3; AM-87.75 ± 3.8; VE-104.66 ± 4.4; and EX-119.48 ± 2.1 for sf. EX and Z250 showed higher st and sf values than the other materials evaluated (p < 0.05), which followed a decreasing trend of mean values. The results confirmed the study hypothesis, showing a positive relation between the material properties examined.

Effect of surface treatments on the bond strength of a zirconia-reinforced ceramic to composite resin

The objective of this study was to evaluate the tensile (sigmat) and shear bond strength (sigmas) of a glass-infiltrated alumina-based zirconia-reinforced ceramic (IZ - Vita In-Ceram Zirconia) to a composite resin, testing the hypothesis that silica coating (SC - Cojet, 3M-Espe) produces higher bond strength values than other ceramic surface treatments. Specimens were fabricated and tested according to the manufacturers' instructions, and to ISO6872 and ISO11405 specifications. Sixty IZ disk specimens were polished through 1 æm and divided into 3 groups (n = 20) according to the following surface treatments: HF - 9.5 percent hydrofluoric acid (Ultradent) for 1 min; SB - sandblasting with 25-æm aluminum oxide particles for 10 s; SC - silica coating for 10 s. Silane (3M-Espe), adhesive (Single Bond, 3M-Espe) and a composite resin cylinder (Z100, 3M-Espe) were applied and polymerized to the treated bonding area (3.5 mm in diameter). Ten specimens from each group (n = 10) were tested for sigmat and ten specimens were tested for sigmas, using a universal testing machine (EMIC DL 2000) at a crosshead speed of 1 mm/min. The data were statistically analyzed by ANOVA and Tukey tests (alpha = 0.05). The mean and standard deviation values (MPa) and statistical groupings for sigmat were: HF - 3.5 ± 1.0a; SB - 7.6 ± 1.2b; and SC - 10.4 ± 1.8c. For sigmas, the values were: HF - 10.4 ± 3.1A; SB - 13.9 ± 3.1B; and SC - 21.6 ± 1.7C (p < 0.05). The groups presented the same statistical ranking of mean values for both test methods. The SC-treated IZ ceramic presented a significant increase in mean bond strength values for both test methods, confirming the study hypothesis.

O objetivo deste estudo foi avaliar a resistência adesiva à tração (sigmat) e ao cisalhamento (sigmas) de uma cerâmica à base de alumina infiltrada por vidro e reforçada com zircônia (IZ- Vita In-Ceram Zircônia) à resina composta, testando a hipótese de que o sistema de silicatização (SC- Cojet, 3M-ESPE) produz valores maiores de resistência adesiva do que demais tratamentos de superfície utilizados. Sessenta corpos-de-prova (cp) em forma de disco da IZ foram fabricados e testados de acordo com as instruções dos fabricantes e as normas ISO6872 e ISO11405. Após polimento até 1 æm, os cp foram divididos em 3 grupos (n = 20) de acordo com o tratamento de superfície aplicado: HF - ácido hidrofluorídrico a 9,5 por cento (Ultradent) por 1 min; SB - jateamento com óxido de alumínio 25 æm por 10 s; SC - silicatização por 10 s. Silano (3M-Espe), adesivo (Single Bond, 3M-Espe) e um cilindro resinoso (Z100, 3M-Espe) foram aplicados na área de adesão (3,5 mm de diâmetro) e fotoativados. Dez cp por grupo (n = 10) foram testados para sigmat e os outros 10 cp para sigmas em uma máquina de ensaios universal (EMIC DL 2000) com velocidade de 1 mm/min. Os resultados foram analisados estatisticamente por ANOVA e Tukey (alfa = 0,05). Os valores médios e desvio padrão (MPa) para sigmat foram: HF - 3,5 ± 1,0a; SB - 7,6 ± 1,2b; SC - 10,4 ± 1,8c. Para sigmas, os resultados foram: HF - 10,4 ± 3,1A; SB - 13,9 ± 3,1B; SC - 21,6 ± 1,7C (p < 0,05). Os grupos mostraram o mesmo ranqueamento estatístico de valores em ambos os testes. A IZ tratada com SC demonstrou aumento significativo na média de resistência adesiva em ambos os testes, confirmando a hipótese inicial.

Resistência flexural e rugosidade superficial de quatro resinas compostas / Flexural strength and surface roughness of four composite resins

Este estudo comparou a resistência á flexão e a rugosidade superficial de quatro resinas compostas (MF - Master Fill®; CT- Concept®; FM- Fill Magic®; Filtek Z250®), testando a hipótese de que esses compósitos apresentam propreidades similares. Vinte corpos-de-prova de cada material foram confeccionados conforme as instruções do fabricante e as normas da ISO 4049, sendo 10 CP em forma de barras (24 x 2 x 2 mm) para od testes de resistência flexural em 3 - pontos (σ) e 10 CP me forma de discos (7 x 2 mm), para a avaliação da rugosidade superficial média (Ra). A σ dos CP foi testada em máquina de ensaio universal (EMIC-2000®) com velocidade de 1 mm/mm. A Ra foi avaliada em rugosímetro (Surfcoder SE1200®). Os resultados de σ e de Ra foram submetidos á análise estatística (Anova e Tukey). Os valores médios e desvio-padrão de σ (MPa) e Ra (µm) foram, respectivamente: Z250 - 119,9 ± 14,9 e 0,138 ± 0,042: MF - 80,4 ± 13,7 e 0,296 ± 0,096; CT - 80,3 ± 9,4 e 0,212 ± 0,043: FM - 97,3 ± 19,3 ± e 0,229 ± 0,057. A média de σ do Z250 foi mais elevada do que os demais grupos (p <0,05), que não apresentaram diferenças estatísticas significativas entre si. Com relação á Ra, a Z250 também apresentou resultados significativamente melhores que os demais grupos, seguida pela CT e FM, que apresentou a maior média de Ra. Pode-se concluir que o compósito microídico Z250 produziu resultados de σ e Ra estatisticamente melhores que os demais materiais testados.